The use of stainless steel pipes is now more and more extensive. Because of its good corrosion resistance, it plays a crucial role in engineering construction. In the process of production, we need to perform solution treatment on stainless steel pipes. The main purpose is to obtain certain Martensite increases the hardness of the product. Let's take a look at the solution treatment of stainless steel pipes:
(1) The intermediate aging method is heated to (760±15) degree after the solution treatment, and the temperature is kept for 90 minutes because Cr23C6 carbides are precipitated from the austenite, which reduces the carbon and alloying elements content in the austenitic 904L stainless steel pipe , the Ms point is raised to 70 degree and then cooled to room temperature to obtain martensite plus ferrite plus retained austenite structure, and the retained austenite is decomposed after aging at 510 degree .
(2) Eftir háhitastillingu og frostmeðferð er lausnin fyrst hituð í 950 gráður í 90 mínútur. Vegna hækkunar á Ms punktinum er hægt að fá lítið magn af martensíti með því að kæla niður í stofuhita; magn martensíts.
(3) Eftir lausnarmeðferð með köldu aflögunaraðferð er köld aflögun framkvæmd við stofuhita. Magn martensíts sem myndast í 904L óaðfinnanlegu pípunni við köldu aflögun er tengt magni aflögunar og samsetningu 904L ryðfríu stáli pípunnar.
Ofangreindar þrjár aðferðir eru algengar aðferðir til lausnarmeðferðar á ryðfríu stáli rörum. Ég vona að þeir geti hjálpað þér.